Pengaruh Solution Heat Treatment terhadap Sifat Fisis dan Mekanik Proses Pengelasan Fssw AA6063-T5
Ciptadi Natawiguna, Nurul Muhayat, Teguh Triyono
Abstract
Friction stir spot welding (FSSW) of aluminum alloy AA6063-T5 will decrease the strength and hardness. Physical and mechanical properties of aluminum alloy can be improved by heat treatment. Heat treatment is affected by temperature and holding time. The heat treatment process used for this research was solution heat treatment with temperature variation 470, 500, 530 oC and holding time 1 and 2 hours. The tests included microstructure test, tensile shear test and vickers hardness test. Result of the research, it was found that Mg2Si particles were precipitated from the grain boundaries part into the aluminum matrix with the coarser size and the distance was increasing as the temperature and the holding time increases. The highest shear tensile strength of 3735,2 N was obtained from the temperature variation of 470 oC and the holding time of 1 hour. The lowest tensile shear strength of 3172,6 N was obtained from temperature variation of 530 oC and 2 hours of holding time. The highest hardness value was obtained of 470 oC variation and 1 hour was 43,7 HVN and the lowest hardness value at 530 oC variation and 2 hours of holding time was 30,1 HVN.
Chi-Sung, J., et al. (2012). "Material properties of friction stir spot welded joints of dissimilar aluminum alloys." Transactions of Nonferrous Metals Society of China 22: s605-s613.
Elangovan, K. dan V. Balasubramanian (2008). "Influences of tool pin profile and tool shoulder diameter on the formation of friction stir processing zone in AA6061 aluminium alloy." Materials & design 29(2): 362-373.
Kamenichny, I., 1969, Short Handbook of Heat Treatment, Moscow Peace Publishers.
Mokhtar Awang, 2007. Simulation of Friction Stir Spot Welding (FSSW) Process: Study of Friction Phenomena.. Department of Mechanical and Aerospace Engineering Morgantown, West Virginia.
R. Sinaga, 1998. Meningkatkan sifat mekanik bahan aluminium paduan (Al-Mg-Si). Prosiding pertemuan ilmiah sains materi III, Serpong.
Shoba, C., et al. (2015). "Influence of dislocation density on the residual stresses induced while machining Al/SiC/RHA hybrid composites." Journal of Materials Research and Technology 4(3): 273-277.
Y. Totik, 2003. The effect of homogenisation treatment on cold deformations of AA 2014 and AA 6063 alloys, Mechanical Engineering Department, Faculty of Engineering, Atatürk University, Erzurum, Turkey.
Zhaohua Zhang, 2011. Effect of welding parameters on microstructure and mechanical propertiesof friction stir spot welded 5052 aluminum alloy. Materials and Design 32 (2011) 4461–4470.
Refbacks
There are currently no refbacks.
Mekanika: Majalah Ilmiah Mekanika
ISSN: 1412-7962 || eISSN: 2579-3144
Address : Jl. Ir Sutami no 36 A, Building I, Faculty of Engineering, Universitas Sebelas Maret, Surakarta.